چکیده
|
A novel nanocomposite including cellulose, chitosan and Ni/NiO was fabricated from
barely wastes, shrimp wastes, and Calotropis procera, respectively. It was characterized by
TEM, SEM, TGA, DTA, FT-IR, BET, EDAX, and elemental analysis. 5e25 nm of Ni/NiO were
dispersed on chitosan and cellulose. The BET isotherms results showed that the Ni/NiO had
a pore size of 11.3 nm with a BET area of 13.8 m2 g1
. While, Chit-Cell@Ni/NiO nano-biocomposite had a pore size of 16.087 nm with a BET area of 15.539 m2 g1
. Then, ChitCell@Ni/NiO bio-nanocomposite was applied to the photodegradation of ciprofloxacin
under sunlight. About 92% of ciprofloxacin could be efficiently degraded within 20 min.
Radical quenching experiments confirmed the contribution of active species was in
descending order of hþ>
OH >
O2
in the Chit-Cell@Ni/NiO system. The possible ciprofloxacin degradation pathway has been proposed according to the intermediates detected
by LC-MS. Also, Chit-Cell@Ni/NiO showed high durability and stability after three-cycle
ciprofloxacin degradation. In short, this study offers an efficient green methodology to
decrease the number of antibiotics in the water system.
|